Chemically cross-linked expanded polyethylene produced without the use of CFCs, with a density of 30 kg/m³ and completely closed cells for thermoacoustic functions.
Standard product Self-adhesive, using a standard acrylic adhesive with good thermal performance up to 80°C. Other types of adhesives can be provided upon request. The standard backing is a 70 μm low-density polyethylene film, but other backings can be used on request.
It finds numerous applications in the construction sector and in industry in general. Particularly suitable for acoustic insulation of impact noise, floating floors and wall noise.
Applications
- Construction
- Interiors
- Industry
Format
- Height: 1000/1500 mm rolls
- Length: from 20 to 200 m depending on the thickness
- Thicknesses: 5 - 10 - 15 mm
Technical features
- Density ISO 845: 28.4 kg/m³
- Longitudinal Tensile Strength ISO 1798: 0.32 MPa
- Transverse Tensile Strength ISO 1798: 0.25 MPa
- Longitudinal Tensile Elongation ISO 1798: 104%
- Transverse Tensile Elongation ISO 1798: 108%
- 10% Compression Set ISO 3386: 24 kPa
- 25% Compression Set ISO 3386: 48 kPa
- 50% Compression Set ISO 3386: 112 kPa
- Residual Deformation 22h Load, 23°C, 25% Compression Set:
- 0.5h after release ISO 1856: 16.4%
- 24h after release ISO 1856: 5.3%
- Flame Propagation Rate DIN 75 200 mm/min: <100
- Thermal Conductivity ISO 2581: 0.039 W/mK
- Dimensional Stability DIN 53 431 °C: 100
- Adhesiveness 1200 g/in:
- Tack 5 cm
- Shear 5 hours
On request
- Other thicknesses
- Can be coupled with a 2mm PVC bubble sheet in 2x1m panels.